铸造高温合金的线膨胀系数α/10-6(1/℃)

发布日期:[13-03-19 21:55:19] 浏览人次:[]

铸造高温合金的线膨胀系数α/10-6(1/℃)
 
牌号
     度
20
~100℃
20
~200℃
20
~300℃
20
~400℃
20
~500℃
20
~600℃
20
~700℃
20
~800℃
20
~900℃
20
~1000℃
20
~1100℃
K211
13.19
13.85
14.56
14.89
15.34
15.68
16.07
16.38
16.68
K213
12.36
13.98
15.22
15.32
15.97
16.35
17.16
18.61
K214
13.2
13.8
14.0
14.5
14.7
14.9
15.0
15.3
16.7
17.6(20
~950℃)
K232
14.8
14.6
14.7
15.0
15.4
15.7
16.1
16.5
K401
10.9
12.9
13.7
16.3
17.7
19.4
21.4
22.4
24.3
K403
11.3
12.3
12.3
12.6
12.9
13.0
13.4
13.8
14.3
15.1
K405
11.6
12.2
12.6
12.9
13.2
13.4
13.8
14.3
15.0
16.0
K406
11.82
12.44
12.94
13.3
13.59
13.93
14.27
14.82
15.48
K409
12.16
12.3
12.6
12.95
13.25
13.65
14.05
14.58
15.25
K412
11.3
12.2
13.1
13.7
14.4
15.1
17.4
19.5
22.1
25.4
K417
13.2
(20~
200.5℃)
13.5
(20~
311℃)
13.5
(20~
469℃)
13.9
(20~
633℃)
14.2
(20~
679℃)
14.4
(20~
711℃)
14.7
(20~
759℃)
15.7
(20~
868℃)
15.9
(20~
900℃)
17.3
(20~
1000℃)
K417G
10.7
11.9
12.9
13.5
14.0
14.2
14.5
14.3
15.2
K418
12.6
12.7
12.9
12.9
13.4
13.7
14.2
14.7
15.5
16.5
K419
12.36
12.44
12.67
12.82
13.06
13.23
13.86
14.04
14.61
15.49
K438
9.78(20~
150℃)
10.7
12.6
14.2
14.6
15.0
15.4
15.6
16.1
16.6
K640
13.9
(20~
315℃)
14.3
(20~
427℃)
14.6
(20~
537℃)
14.7
(20~
570℃)
15.0
(20~
650℃)
15.6
(20~
826℃)
15.9
(20~
870℃)
      温度为:20~100℃、100~200℃、200~300℃、300~400℃、400~500℃、500~600℃、600~700℃、700~800℃、800~900℃、900~1000℃。
www.mapeng.net 马棚网
www.mapeng.net
文章作者:未知 | 文章来源:网络 | 责任编辑:cupcup1982 | 发送至邮箱: | 加入收藏:
本文关键字:机械标准  机械行业标准
本文所属专题:机械设计手册—钢 
关于我们 | 站点导航 | 使用帮助 | 友情链接 | 广告服务 | 免责声明 | 新手上路
设为首页 | 加入收藏 | 在线留言 | 马棚网QQ群:{92562572}{102901272}{333259257} | 交流QQ: 客户服务 客户服务 客户服务